Au-decorated Sb 2 Se 3 photocathodes for solar-driven CO 2 reduction
A nano-structured photoelectrode made from Sb 2 Se 3 was prepared and was utilized for CO 2 reduction. Au nanoparticle catalysts were deposited to facilitate CO formation.