Effect of pH in the hydrothermal preparation of monoclinic tungsten oxide
This paper presents the preparation of monoclinic WO3 by a one-step hydrothermal method. The effect of very acidic pH (0.1) and the significance of various additives (CH3COOH, NaClO4, Na2SO4) were investigated. To clarify the role of pH on the obtained crystal structure and morphology, every synthes...
Elmentve itt :
| Szerzők: | |
|---|---|
| Dokumentumtípus: | Cikk |
| Megjelent: |
2020
|
| Sorozat: | JOURNAL OF SOLID STATE CHEMISTRY
281 |
| doi: | 10.1016/j.jssc.2019.121044 |
| mtmt: | 31042183 |
| Online Access: | http://publicatio.bibl.u-szeged.hu/18405 |
| LEADER | 01963nab a2200289 i 4500 | ||
|---|---|---|---|
| 001 | publ18405 | ||
| 005 | 20200319114757.0 | ||
| 008 | 200319s2020 hu o 0|| zxx d | ||
| 022 | |a 0022-4596 | ||
| 024 | 7 | |a 10.1016/j.jssc.2019.121044 |2 doi | |
| 024 | 7 | |a 31042183 |2 mtmt | |
| 040 | |a SZTE Publicatio Repozitórium |b hun | ||
| 041 | |a zxx | ||
| 100 | 2 | |a Nagyné Kovács Teodóra | |
| 245 | 1 | 0 | |a Effect of pH in the hydrothermal preparation of monoclinic tungsten oxide |h [elektronikus dokumentum] / |c Nagyné Kovács Teodóra |
| 260 | |c 2020 | ||
| 300 | |a Azonosító: 121044-Terjedelem: 7 p | ||
| 490 | 0 | |a JOURNAL OF SOLID STATE CHEMISTRY |v 281 | |
| 520 | 3 | |a This paper presents the preparation of monoclinic WO3 by a one-step hydrothermal method. The effect of very acidic pH (0.1) and the significance of various additives (CH3COOH, NaClO4, Na2SO4) were investigated. To clarify the role of pH on the obtained crystal structure and morphology, every synthesis using pH 1 were repeated, and the effect of temperature, using 180 and 200 °C, was also studied. All samples prepared at pH 0.1 were pure, well crystallized monoclinic WO3 independently from the temperature, the presence and the quality of the additives. At 180 and 200 °C, applying CH3COOH and NaClO4 resulted nanosheets similar in size. With Na2SO4 additive at 180 °C sheets, at 200 °C sheets and also rods formed indicating that SO4 2− was a capping agent only at 200 °C. For comparison, at pH 1 at both temperatures the crystalline phases and the morphologies varied depending on the type of the additive. © 2019 The Authors | |
| 700 | 0 | 1 | |a Lukács István Endre |e aut |
| 700 | 0 | 1 | |a Szabó Anna |e aut |
| 700 | 0 | 1 | |a Hernádi Klára |e aut |
| 700 | 0 | 1 | |a Igricz Tamás |e aut |
| 700 | 0 | 2 | |a Nagyné László Krisztina |e aut |
| 700 | 0 | 2 | |a Szilágyi Imre Miklós |e aut |
| 700 | 0 | 2 | |a Pokol György |e aut |
| 856 | 4 | 0 | |u http://publicatio.bibl.u-szeged.hu/18405/1/JSolStateChem2812020121044.pdf |z Dokumentum-elérés |